If your sending your bits out for plating. Make sure they get baked.
Spring steel needs to be baked to keep from getting brittle.
Seems my batches are inconsistent at being baked so I'm going to make sure I request it next time I have springs in the batch. I haven't had one of the c clips break yet. But I've heard stories.

[bbrock]

If your sending your bits out for plating. Make sure they get baked.
Spring steel needs to be baked to keep from getting brittle.
Seems my batches are inconsistent at being baked so I'm going to make sure I request it next time I have springs in the batch. I haven't had one of the c clips break yet. But I've heard stories.

@cary , curious if you use any kind of acid to clean spring steel before having them plated and baked. I've read that acid clean can contribute to hydrogen embrittlement and I have used vinegar to dissolve heavy rust off many parts. My hope is that this kind of exposure to a mild acid isn't a problem. I also know the parts are typically dipped in strong acid prior to plating so I'm thinking as long as they are baked at the end of the process, it should be okay.

BTW, the US military found that long term exposure to Simple Green also causes hydrogen embrittlement. I learned that on a woodworking site because Simple Green is commonly used to clean pitch off of saw blades. Works great, but if you soak the blade overnight, you are asking for trouble.

[mepstein]

If your sending your bits out for plating. Make sure they get baked.
Spring steel needs to be baked to keep from getting brittle.
Seems my batches are inconsistent at being baked so I'm going to make sure I request it next time I have springs in the batch. I haven't had one of the c clips break yet. But I've heard stories.

@cary , curious if you use any kind of acid to clean spring steel before having them plated and baked. I've read that acid clean can contribute to hydrogen embrittlement and I have used vinegar to dissolve heavy rust off many parts. My hope is that this kind of exposure to a mild acid isn't a problem. I also know the parts are typically dipped in strong acid prior to plating so I'm thinking as long as they are baked at the end of the process, it should be okay.

BTW, the US military found that long term exposure to Simple Green also causes hydrogen embrittlement. I learned that on a woodworking site because Simple Green is commonly used to clean pitch off of saw blades. Works great, but if you soak the blade overnight, you are asking for trouble.

In the cycling world, we learned that soaking the chain in simple green will weaken it and the plates will crack and break.